SiO2的甲硅烷基化对钴基催化剂费-托合成催化性能的影响OA北大核心CSCDCSTPCD
Silylation of SiO2 and its influence on the properties of cobalt-based catalysts for Fischer-Tropsch synthesis
利用甲硅烷基化作用制得了不同疏水程度的SiO2载体,采用等体积浸渍法制备了质量分数为5％的一系列负载型钴催化剂.结合FT-IR、29Si CP MAS NMR、BET、XRD、Raman、XPS和H2-TPR等表征手段,考察了SiO2甲硅烷基化对钴基催化剂物相结构、还原行为以及费-托合成催化性能的影响.催化剂在固定床反应器中,在p=2.0 MPa、t=240℃、n(H2 )/n( CO)=2和GHSV=1000h-1的条件下进行评价.结果表明,随…查看全部>>
Silylated SiO2 with different hydrophobicities was prepared before the impregnation of cobalt precursor to obtain Co-based catalysts in Fischer-Tropsch synthesis. The effect of silylation on the crystallite structure and reduction behaviors of the resultant cobalt catalysts was investigated by FT-IR, 29Si CP MAS NMR, N2 sorption, XRD, Raman, XPS, and H2-TPR; their catalytic performance in Fischer-Tropsch synthesis was evaluated in a fixed-bed reactor under 2…查看全部>>
石利红;李晓峰;李德宝;孙予罕
山西大学化学化工学院,山西太原030006中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001太原大学外语师范学院自然科学基础部,山西太原030012中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001
化学
钴二氧化硅甲硅烷基化疏水费-托合成
cobalt SiO2 silylation hydrophobic Fischer-Tropsch synthesis
《燃料化学学报》 2012 (6)
737-742,6
评论