基于聚噻吩/聚己内酯共混物的有机薄膜晶体管OA北大核心CSCDCSTPCD
Organic Thin Film Transistors Based on Blends of Poly (3-hexylthiophene) and Polycaprolactone
选择聚3-己基噻吩(P3HT)/聚己内酯(PCL)双晶共混体系制备了不同配比的共混物有机薄膜晶体管.电学性能研究发现,随着共混物中P3HT含量降低,薄膜晶体管的场效应迁移率、开关电流比和阈值电压等性能缓慢降低.当P3HT质量分数为40％时,共混物薄膜仍具有较好的场效应性能,迁移率为0.008 cm2·V-1·s-1,开关电流比为5×103,阈值电压为45.5 V.原子力显微镜测试结果表明:共混物成膜时发生明显的垂直相分离,在界面处形成连续的半导体层,有利于载流子传输.
A blending crystalline system containing poly ( 3-hexylthiophene) and polycaprolactone was investigated. The electric measurements reveal that the field-effect performances of blend films, such as mobility, on/off current ratio and threshold voltage, decrease slowly with P3HT content reducing. However, the devices still have relatively good performance even P3HT content was 40%. According to the AFM studies, vertical phase separation occurs in the blend film…查看全部>>
王晓鸿;邱龙臻
特种显示技术教育部重点实验室,特种显示技术国家工程实验室,现代显示技术省部共建国家重点实验室培育基地,合肥工业大学光电技术研究院,安徽合肥230009特种显示技术教育部重点实验室,特种显示技术国家工程实验室,现代显示技术省部共建国家重点实验室培育基地,合肥工业大学光电技术研究院,安徽合肥230009
信息技术与安全科学
有机薄膜晶体管半导体/绝缘聚合物相分离电性能
organic thin-film transistors ( OTFTs) semiconducting/insulating blend phase separation electric performance
《发光学报》 2012 (8)
喷墨打印聚合物共混物薄膜相分离行为及其在晶体管中的应用
857-862,6
973计划前沿专项(2010CB334704,2012CB723406)国家自然科学基金(21174036,51103034)资助项目
评论