CSP-冷轧热镀锌板表面线状缺陷特征及形成原因OA北大核心CSCDCSTPCD
Characteristic and Forming Reason of a Sliver-type Defect on the Surface of CSP-hot Galvanized Sheets
表面长条线状缺陷导致CSP-冷轧热镀锌板质量降低,利用金相显微镜、XRD和扫描电镜对缺陷的形貌与组成等进行了分析.长条线状缺陷的形成原因是:在CSP热轧阶段形成的氧化铁皮(FeO)被压入基板,并在冷轧时被拉长、碾碎,冷轧后,这些氧化物呈现出点链状直线分布,镀锌增强了其与基体的差别,凸现出长条线状缺陷.最后,据此提出了减少氧化铁皮压入的措施,抑制了长条线状缺陷的产生.
The quality of the CSP-hot galvanized sheets was decreased by some sliver-type surface defects. The morphology, structure and component of the defect were analyzed by using optical microscope, XRD and SEM-EDS. The results showed that the oxides (FeO) formed in CSP hot rolling led to the defect. The oxides were pressed in or e-longated in the surface layer of the steel in a centimeter-scale to meter-scale during hot rolling and cold rolling. Finally the oxide…查看全部>>
魏远征;李书黎;周学俊;苗景国;宋书鹏;吴润
武汉科技大学 材料与冶金学院,武汉 430081武汉钢铁(集团)公司,武汉 430083武汉科技大学 材料与冶金学院,武汉 430081武汉科技大学 材料与冶金学院,武汉 430081武汉科技大学 材料与冶金学院,武汉 430081武汉科技大学 材料与冶金学院,武汉 430081
化学化工
长条状缺陷CSP热镀锌板
sliver-type defect CSP hot galvanized sheets
《表面技术》 2012 (5)
Al系十次准晶与金属Cu间界面的结构和性能研究
93-95,113,4
国家自然科学基金资助项目(50901053)
评论