电池2012，Vol.42Issue(5)：274-276,3.
锂离子电池高能量密度负极配方
The formula of anode with high energy density for Li-ion battery
汪国红 1魏思伟 1黄凯军 1黄少波1
作者信息
- 1. 深圳市美拜电子有限公司,广东深圳518000
- 折叠
摘要
Abstract
Charge-discharge characteristics of the Li-ion battery with the anode of 94.5% mass content of active material and 4% mass content of CMC/SBR(mass ratio 3 : 5), or 96.5% mass content of active material and 2.0% or 2.5% mass content of acry-lonitrile multi-copolymer LA133 were compared. The cell expansion,cycle performance and safety performance were investigated. The cell with the anode of 2.5% LA133 had the best comprehensive performance,exhibited a energy density of 455 Wh/L at the current of 1.00 C (3.0 ～ 4.2 V), 10.44% higher than the cell with the anode of 4.0% mass content of CMC/SBR. The capacity retention was more than 91% after 300 cycles at the current of l.00 C (3.0～4.2 V) .Environment and safety test showed that the battery had high environment adaptability and reliability.关键词
锂离子电池/高能量密度/负极配方/丙烯腈多元共聚物LA133Key words
Li-ion battery/ high energy density/ anode formula/ acrylonitrile multi-copolymer LA133分类
信息技术与安全科学引用本文复制引用
汪国红,魏思伟,黄凯军,黄少波..锂离子电池高能量密度负极配方[J].电池,2012,42(5):274-276,3.