硅酸盐通报2012，Vol.31Issue(5)：1298-1302,5.
B2O3对SiO2-Al2O3-MgO系统高强玻璃纤维性能的影响
The Influence of B2O3 Content on the Properties of SiO2-Al2O3-MgO System High Strength Glass Fibers
摘要
Abstract
High strength glass fibers have the characteristics of light weight, high strength, high temperature resistantance and high cost performance, so it has been widely applied in the composite materials. In this paper,the influences of B2O3 on the properties of high strength glass fiber were studied by the way of testing the stretching, erosion, viscosity, infrared properties of the samples with different B2O3 contents. The results showed that the tensile strength is enhanced and the high temperature vioscity is decreased along when the concentration of B2O3 is was increased. To a certain extent, it not only improve the fibers'process performance, but enhance its mechanical properties.关键词
高强玻璃纤维/氧化硼/断裂韧性/拉伸强度/粘度Key words
high strength glass fiber/boron oxide/fracture toughness/tensile strength/viscosity分类
化学化工引用本文复制引用
宁伟,陈群涛,汪庆卫,王宏志,石冬霓..B2O3对SiO2-Al2O3-MgO系统高强玻璃纤维性能的影响[J].硅酸盐通报,2012,31(5):1298-1302,5.基金项目
资助上海市重点学科建设项目资助(B603) （B603）