化工学报2012，Vol.63Issue(10)：3365-3371,7.DOI:10.3969/j.issn.0438-1157.2012.10.051
聚硼硅氧烷阻燃剂的合成工艺及其在聚碳酸酯中的应用
Synthesis of polyborosiloxane flame retardant and its application to polycarbonate
摘要
Abstract
Polyborosiloxane (PB) was synthesized through two-step reaction by using alkoxysilanes and boric acid as raw materials and synthesis optimization was studied through adjusting boric acid /silane molar ratio, condensation temperature and hydrolysis time. The effect of PB on flame retardancy and physical properties of polycarbonate (PC) was investigated. The results showed that strict control of boric acid/silane molar ratio and condensation temperature was the key to preparation of high efficiency flame retardant PB. When boric acid /silane molar ratio was 1:1, and condensation temperature was 100℃ , PB had the best flame retardancy on PC. After adding 5% (mass) of PB, LOI of PC could increase from 26% to 39. 4% . Addition of PB could decrease thermal degradation onset temperature of PC. However PB decreased mass loss rate of PC and increased degradation residue of PC at 800℃ . PB could promote the formation of char residue which could serve as a good insulating barrier to reduce the radiant heat of flame and lower decomposition rate of PC. Addition of PB increased tensile strength and flexural strength of PC, but decreased impact strength of PC. In addition, PB had little effect on optical properties of PC, and the PC/PB composites were still transparent.关键词
聚硼硅氧烷/聚碳酸酯/阻燃性能/物理性能Key words
polyborosiloxane/ polycarbonate/ flame retardancy property/ physical property分类
化学化工引用本文复制引用
周文君,宋健,陈友财,王雪芹,张敬礼..聚硼硅氧烷阻燃剂的合成工艺及其在聚碳酸酯中的应用[J].化工学报,2012,63(10):3365-3371,7.基金项目
浙江省公益技术应用研究项目(2011C31047). （2011C31047）