表面技术2012，Vol.41Issue(6)：78-81,107,5.
彩色不锈钢板电化学褪膜工艺研究
Study on Film-fading Process of Uneven Colored Stainless Steel
摘要
Abstract
The film-fading technology by electrolytic process of uneven colored stainless steel plate in the production process was studied. The quality of film-fading technology was evaluated by brightness of sample and performance of recolored film-fading sample. The suitable solution of film-fading technology was evaluated by mass loss rate method and optical reflectance method, effect of temperature and current density on optical reflectance ratio of film-fading samples were discussed; The color uniformity, corrosion resistance, crocking resistance of recolored film-fading sample were tested. The experimental results show that the color difference is less than 0.7, the weightlessness corrosion rate is 11.5831 g/(m2 · h), the rubbing times up to 1950. They all indicate that the performance of recolored film-fading sample is as excellent as the conventional coloring sam-pie.关键词
不锈钢/电化学褪膜/再着色Key words
stainless steel/ film-fading technology by electrolytic process/ recolor分类
矿业与冶金引用本文复制引用
黄凤祥,满瑞林,胡俊利,刘小勤,刘晶晶..彩色不锈钢板电化学褪膜工艺研究[J].表面技术,2012,41(6):78-81,107,5.基金项目
中南大学中央高校基本科研业务费专项资金资助(2012zzts054) （2012zzts054）