聚硅酸铝铁絮凝剂的制备及其性能研究
Study on Preparation of Poly Aluminum-ferric Silicate Flocculants and its Performance
摘要
Abstract
Poly aluminum ferric silicate was prepared from high - alumina - bearing fly ash, sulfu-ric acid cinder and industrial waste acid. Based on the chemical and physical property of the high - alumina fly ash, the extraction process of silica, aluminium and ferrum of " solid - phase pyroly-sis and acid leaching" was established by taking trona as cosolvent. The best synthesis conditions of poly aluminum - ferric silicates was reached when molar ratio of silicate and alumina is 1 : 0.7, molar ratio of silicate and alumina is 1 : 0.5, pH value is 2, polymerization temperature is 60?. Finally, the product was characterized using XRD, IR and SEM. The result shows that the poly a-luminum ferric silicate from this fabrication process was of good polymerization and big polymer size. Compared with the traditional flocculants, this new product has better flocculation performance.关键词
高铝粉煤灰/聚硅酸铝铁/酸溶/聚合条件/助溶剂/絮凝性能Key words
high - aluminium fly ash/ poly aluminum ferric silicate/ acid leaching/ polymerization conditions/ cosolvent/ flocculation performance分类
化学化工引用本文复制引用
范剑明,吉仁塔布,李诚诚,季伟..聚硅酸铝铁絮凝剂的制备及其性能研究[J].矿产保护与利用,2012,(4):37-40,4.基金项目
内蒙古自治区自然科学基金重点项目(2010ZD04) （2010ZD04）