华东师范大学学报（自然科学版）Issue(1)：115-120,6.DOI:10.3969/j.issn.1000-5641.2013.01.014
外镀铜层玻璃包裹丝的巨磁阻抗效应
Giant magneto-impedance on glass-coated microwires with copper layer
摘要
Abstract
The amorphous wires of nominal compositions Fe73.0 Cu1.0 Nb1.5 V2.0 Si13.5 B9.0 were prepared by glass-coating melt-spinning method. Then, the wires were annealed at 480~650 ℃ for 30 min in nitrogen atmosphere. The composite wires with copper layer using electroless deposition were produced, a thin layer of copper deposited onto the microwires annealed at 570 ℃. The morphology of composite microwires was observed using SEM. The giant magnetoimped-ance effect on the samples was investigated. The results show that soft magnetic properties of the specimen can improve its MI ratio. The electromagnetic interactions between the ferromagnetic core and the copper layer can also affect MI ratio.关键词
巨磁阻抗效应/化学镀/趋肤效应/软磁特性Key words
giant magneto-impedance effect/ electroless deposition/ skin effect/ soft magnetic properties分类
数理科学引用本文复制引用
王蕊丽,阮建中,孔祥洪,杨渭,王江涛,赵振杰..外镀铜层玻璃包裹丝的巨磁阻抗效应[J].华东师范大学学报（自然科学版）,2013,(1):115-120,6.基金项目
上海市科委项目(10520706300) （10520706300）
大学物理创新实验(B-8606-10-0001-14) （B-8606-10-0001-14）
大学物理基础实验室建设(B-5109-11-0007) （B-5109-11-0007）