人工晶体学报2013，Vol.42Issue(2)：305-309,315,6.
溶胶-凝胶法制备TiO2-C纳米复合材料的研究
Preparation of TiO2-C Nano-composite Materials by Sol-Gel Method
摘要
Abstract
TiO2-C nanocomposite materials were prepared by using sol-gel process, which were characterized by XRD, SEM and TEM. Results showed that the precursors of TiO2 and carbon could be co-gelated soon at room temperature by adding propylene oxide as gelation initiator. TiO2 grain grows up after it is heated at 600 ℃ for 3 h, and its characteristic peak is more clear. The crystal structure of TiO2 is anatase. Ethyl acetoacetate as a complexing agent is beneficial for the formation of the gels. The pore volume and the pore diameter in the TiO2-C nanocomposite materials increase with the increasing amount of the ethyl acetoacetate.关键词