β-环糊精聚合物/二氧化钛杂化电流变材料的制备及性能
Preparation and electro-rheological properties of β-cyclodextrin polymer/titanium dioxide hybrid materials
摘要
Abstract
The β-CDP was obtained by the polymerization of allyl-β-CD and AA with azodiisobutyronitrile (AIBN) as initiator, and β-CDP/TiO2 hybrid materials were subsequently prepared by the reaction between β-CDP and butyl titanate. The results of FT-IR,SEM and XRD show that the chemical bond is formed between the TiO2 phases and the polymer matrix in the hybrid, and the organic and inorganic components were well dispersed homogeneously with each other. The results indicated that the electro-rheological (ER) properties of β-CDP/TiO2 was much better than that of pure β-CD and β-CDP. In addition, the effect of ER is best when 40% butyl titanate was introduced into β-CDP.关键词
β-环糊精/钛酸丁酯/电流变效应Key words
β-cyclodextrin/ butyl titanate/ electro-rheological effect分类
生物科学引用本文复制引用
鲁琦,高子伟,韩肖慧,李子美,孙华明..β-环糊精聚合物/二氧化钛杂化电流变材料的制备及性能[J].陕西师范大学学报（自然科学版）,2013,41(2):54-58,5.基金项目
国家自然科学基金资助项目(21041004,20771071) （21041004,20771071）
教育部新世纪优秀人才支持计划项目(NCET-07-0528) （NCET-07-0528）
中央高校基本科研业务费专项资金项目(GK200902001,GK261003). （GK200902001,GK261003）