表面技术2013，Vol.42Issue(2)：84-88,5.
电沉积聚8-羟基喹啉膜及其耐蚀性的研究
Electrodeposition of Poly-8-hydroxyquinoline Films and Its Corrosion Resistance Performance
摘要
Abstract
The poly-8-hydroxyquinoline was firstly prepared by cyclic voltammetry. The mechanism of polymerization was speculated, and the composition of the polymer film was studied with infrared spectres-copy. Tafel testing was used in order to optimize the treatment for electrodeposition. The result shows that; the best condition of cyclic voltammetry method to synthesize corrosion-resistance polymer film is; the concentration of 8-hydroxyquinoline is 0. 002 mol/L, sodium hydroxide is 0. 4 mol/L, the scan rate is 30 mV/s, and scan 8 laps. A bright and smooth yellow film is obtained and the corrosion-resistance performance of the nickel plating work piece processes under the optimized condition was improved significantly.关键词
电沉积/聚8-羟基喹啉/防腐蚀/循环伏安法Key words
electrodeposition/ poly-8-hydroxyquinoline/ corrosion-resistance/ cyclic voltammetry分类
化学化工引用本文复制引用
刘小勤,曾冬铭,徐钦建,黄凤祥,刘中兴..电沉积聚8-羟基喹啉膜及其耐蚀性的研究[J].表面技术,2013,42(2):84-88,5.基金项目
中南大学中央高校基本科研业务费专项资金资助(2012zzts054) （2012zzts054）