铸造2013，Vol.62Issue(4)：292-295,4.
高矿化度水下铝锰合金腐蚀摩擦磨损性能的研究
Study on Corrosion, Friction and Wear Performance of Al-Mn Alloy Under High Salinity Water
摘要
Abstract
The corrosion, friction and wear performance of Al-0.90%Mn, Al-2.15%Mn and Al-2.86%Mn alloy were measured with the M-2000 type tester, and the wear surface morphology was observed by LED 1430 VP type scanning electron microscopy. The results show that under high salinity water, the attrition of Al-Mn alloy is more serious with the increase of the load; under the high-speed condition, the material attrition is more serious than that under the low-speed condition. With the manganese content increasing, the wear resistance of the sample become better.关键词
铝锰合金/腐蚀/摩擦/磨损/磨痕形貌Key words
Al-Mn alloy/ corrosion/ friction/ wear/ wear surface morphology分类
矿业与冶金引用本文复制引用
徐婷,刘炳..高矿化度水下铝锰合金腐蚀摩擦磨损性能的研究[J].铸造,2013,62(4):292-295,4.基金项目