Study on Preparation and Properties of Geopolymer Porous Materials Based on Clay
摘要
Abstract
Clay and industrial water glass were used as raw materials to prepare a light geopolymers porous material at high temperature in this article.Experiment results showed that the volume density of porous material was between 0.32 g/cm3 to 1.0 g/cm3,and the compressive strength was between 0.46 MPa to 2.68 MPa.From the microstructure analysis on the materials,it can be seen that the properties,such as compressive strength and volume density,have a great relationship with the pore structure,pore size and uniformity of the pore.关键词
地质聚合物/多孔材料/粘土/抗压强度Key words
geopolymer/ porous materials/ clay/ compressive strength分类