理化检验-物理分册2013，Vol.49Issue(6)：410-412,3.
压气机一级转子叶片缺陷分析
Defects Analysis on First Stag Rotor Blade of Compressor
刘卫东1
作者信息
- 1. 四川成发航空科技股份有限公司理化检测中心,成都610500
- 折叠
摘要
Abstract
Abnormal conditions to the first stage rotor blade of a compressor were found when magnetic powders inspecting after polished,and then macrostructure examination to the abnormal position was performed.It is found that there were multiple-lines defects similar to cracks on the convex airfoil surface of the blade along with longitudinal direction,and then means of metallographic examination and energy spectrum analysis were employed to investigate the formation reasons of the defects.The results indicate that the defects of the blade were induced by the slags carried from the smelting process of the raw material,and the slags were crushed during the following pressure deformation process and distributed in banded shape along the longitudinal direction at local of the blade.关键词
转子叶片/缺陷/夹渣Key words
rotor blade/ defect/ slag分类
矿业与冶金引用本文复制引用
刘卫东..压气机一级转子叶片缺陷分析[J].理化检验-物理分册,2013,49(6):410-412,3.