林业科技开发2013，Vol.27Issue(4)：102-105,4.DOI:10.3969/j.issn.1000-8101.2013.04.027
稻草刨花板薄木贴面工艺
Study on manufacturing process of veneer faced rice straw particleboard
摘要
Abstract
Orthogonal tests were performed to investigate the manufacturing process of veneer faced rice straw particleboard.The results showed that it was feasible to veneer rice straw particleboard.When the board was faced with 0.2 mm thick ash veneer and glued with PVAC with an amount of 100 g/m2,the optimal hot pressing parameters were as follows:pressure 0.7 MPa,temperature 100℃,time 120 s.When GB-3 was chosen as adhesive and all the other conditions were kept unchanged,the optimal hot pressing parameters were:pressure 0.8 MPa,temperature 90℃,time 180 s.When the board was faced with 0.6 mm thick white oak veneer and glued with PVAC with an amount of 120 g/m2,the optimal hot pressing parameters were:pressure 0.8 MPa,temperature 90℃,time 240 s.When the adhesive was changed to GB-3 and all the other conditions were kept unchanged,the optimal hot pressing parameters were:pressure 0.7 MPa,gkv temperature 90℃,time 180 s.关键词
稻草刨花板/薄木/贴面Key words
rice straw particleboard/ veneer/ surface overlaying引用本文复制引用
饶鑫,杨静,孙淑英..稻草刨花板薄木贴面工艺[J].林业科技开发,2013,27(4):102-105,4.基金项目
河南省软科学研究项目(编号:132400410650) （编号:132400410650）
江苏农林职业技术学院科研项目(编号:2010C01). （编号:2010C01）