焙烧温度对K-Cu/Zn/La/ZrO2催化剂上异丁醇合成的影响OA北大核心CSCDCSTPCD
Effect of calcination temperature on performance of K-Cu/Zn/La/ZrO2 for isobutanol synthesis
采用共沉淀法制备了Cu/Zn/La/ZrO2催化剂,并浸渍K对其进行改性.以合成气合成异丁醇为探针反应,考察了焙烧温度对K-Cu/Zn/La/ZrO2催化剂合成反应的影响.采用XRD、TG、BET、NH3-TPD、H2-TPR、Raman及XPS等手段表征了催化剂的结构和表面性质.结果表明,催化剂体相结构、比表面积与其催化活性没有直接关系；催化剂表面强酸中心的存在不利于异丁醇的生成；Cu-Zn-Zr活性组分间协同作用对催化剂活性影响很大,450℃…查看全部>>
K-promoted Cu/Zn/La/ZrO2 catalyst were prepared by coprecipitation methods.Hydrogenation of CO was used as a probe reaction to investigate the catalytic performance.Structure and surface properties of K-Cu/Zn/La/ZrO2 catalysts were characterized by XRD,TG,BET,NH3-TPD,H2-TPR,Raman and XPS technics.The results indicated that structure and specific surface had no direct relationship with the catalyst activity.Strong acidic sites of catalyst surface were not goo…查看全部>>
武应全;解红娟;寇永利;谭理;韩怡卓;谭猗生
中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001中国科学院大学,北京100049中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001中国科学院大学,北京100049太原理工大学化学化工学院,山西太原030024
化学
合成气异丁醇焙烧温度铜氧化锆
syngas isobutanol calcination temperature copper zirconia
《燃料化学学报》 2013 (7)
868-874,7
中国科学院山西煤炭化学研究所前瞻性布局项目(2011SQZBJ13)国家重大科学仪器设备开发专项(2011YQ120039).
评论