西华大学学报（自然科学版）Issue(1)：28-30,3.DOI:10.3969/j.issn.1673-159X.2014.01.007
氧化锆球体上的铝膜机械球磨法制备及工艺研究
Preparation of Al Film by Mechanical Coating Technique with ZrO2 Balls
摘要
Abstract
The Al film was fabricated using mechanical coating technique (MCT) on ZrO2 ceramic balls.The microstructure and composition of the film were examined by SEM and EDS .The effects of milling time, milling speed and ball-to-powder mass ratio on the thickness were investigated by L9(34) orthogonal test.The results showed that the factors, which affected the film thickness, were the ball milling rotating speed , ball milling time , and ball-to-powder mass ratio , from maximum to minimum .The maximum film thick-ness reached to 50μm and it was prepared if milling time is 10h, milling speed is 250r/min., and ball-to-powder mass ratio is 7∶1. The Al film was compacted, with low oxygen content and high purity .It was mechanically bonded well with ZrO 2 balls.关键词
铝膜/机械球磨法/真空烧结/工艺参数/膜厚Key words
Al film/MCT/vacuum sintering/process parameters/film thickness分类
通用工业技术引用本文复制引用
查五生,吴开霞,陈立甲,周淑容..氧化锆球体上的铝膜机械球磨法制备及工艺研究[J].西华大学学报（自然科学版）,2014,(1):28-30,3.基金项目
西华大学创新基金 （）