物理学报Issue(3)：030702-1-030702-7,7.DOI:10.7498/aps.63.030702
30CrMnSiNi2A晶格参量的测量及回复规律研究
Variation of parameters and recovery in crystal lattice of 30CrMnSiNi2A
摘要
Abstract
Aiming at the peaks overlapping in the field of X-ray diffraction, a new method for peaks separation was developed, and the parameters and recovery behaviors of crystal lattice of 30CrMnSiNi2A were investigated using RU-200V X-ray powder diffractmeter, by which the relationship between lattice parameters and carbon content at different tempering temperatures was obtained. Results show that the variation of lattice parameters of 30CrMnSiNi2A is consistent with high-carbon martensite on the whole, however there are some differences in the rate of change. The lattice parameter a is independent of carbon content, and slightly decreases with the rise of tempering temperature, while the amplitude of change for the lattice parameter c and carbon content is large, and a steep drop is observed in the process of quenching to the tempering temperature at 180 ◦C, while the amplitude becomes flat aferwards for a higher tempering temperature.关键词
马氏体/晶格参量/碳含量/回火Key words
martensite/crystal lattice parameter/carbon content/tempering引用本文复制引用
袁书强,沈正祥,周春华,刘峰涛,王芳,杨辉,陈炯..30CrMnSiNi2A晶格参量的测量及回复规律研究[J].物理学报,2014,(3):030702-1-030702-7,7.基金项目
宁波市科技攻关项目(批准号:2009B10011)资助的课题 （批准号:2009B10011）