陕西科技大学学报（自然科学版）Issue(2)：36-40,45,6.
耀州窑月白釉的复仿制及呈色机理研究
Preparation and coloring mechanism analysis of pale green glaze
摘要
Abstract
In this work ,feldspar ,quartz ,calcite and talc were used as raw materials to obtain the basic composition of the pale green glaze by the triangle batching method .Then ,the effects of the clay and iron oxide addition on the coloring of the fabricated glazes were inves-tigated and the similar products with ancient ceramics were fabricated .The phase composi-tion and microstructure of the imitation pale green glaze and the ancient glaze were discussed by the X ray diffraction (XRD ) and scanning electron microscopy/energy dispersive spec-trometry (SEM/EDS) .The results show that the green glaze with high opacity can be ob-tained when mole ratio of Si to Ca is in the region of 5 .35~10 .17 .The color of the imitation pale green glaze is developed from bluish yellow to bluish green with increase of iron oxide content ,and the glaze color is from green to yellow with increasing the clay content .The fab-ricated pale green glaze has a similar microstructure with the ancient ceramics .But the crys-talline phase content is less and the size of bubbles is smaller and dispersed more uniform than those in the ancient ceramics ,w hich are more favorable for the coloring of the pale green g laze .关键词
月白釉/微观结构/呈色机理Key words
pale green glaze/ingredients/coloring mechanism引用本文复制引用
朱建锋,施佩,王芬,董龙龙,吕臣敬..耀州窑月白釉的复仿制及呈色机理研究[J].陕西科技大学学报（自然科学版）,2014,(2):36-40,45,6.基金项目
国家自然科学基金项目（51072109）；陕西省科技厅科技统筹创新工程计划项目 （）