控轧工艺对301奥氏体不锈钢组织及性能的影响
Effect of Controlled Rolling Process on Microstructur and Properties of 301 Austenitic Stainless Steel
周鹤1
作者信息
- 1. 郑州大学材料科学与工程学院,河南郑州450001;河南水利与环境职业学院,河南郑州450011
- 折叠
摘要
Abstract
The cold rolling experimental of 0.99 mm thick 301 stainless steel sheet was conducted,and the room-temperature tensile test,the Vickers hardness measurement,the microstructure observation and the X-ray diffraction analysis were conducted.The results show that the deformation-induced martensite phase transformation cause the increase of the hardness and strength of 301 stainless steel,which increases with the increase of deformation.关键词
301不锈钢薄板/冷轧/应变诱导马氏体相变/加工硬化Key words
301 stainless steel sheet/ cold rolling/ strain induced martensitic transformation/ work hardening分类