表面技术Issue(4)：115-118,134,5.
Fe3 O4催化纤维素水热法制备 Fe2 O3/碳纳米复合材料
Preparation of Fe2 O3/Carbon Nano-material by Hydrothermal Carbonization of Cellulose Using Fe3 O4 as Catalyst
摘要
Abstract
Objective To obtain Fe2 O3 / carbon nano material in a relatively mild environment. Methods Cellulose was hydro-thermally treated using nano Fe3 O4 as catalyst, the product was analyzed using scanning electron microscopy, transmission electron microscopy and X-ray diffraction. Results After 3 h of hydrothermal treatment, Fe2 O3 / carbon nano material with a size of 150 nm and a rhombic shape was obtained. Conclusion By hydrothermal treating using nano Fe3 O4 as catalyst, cellulose was carbonized and formed a core-shell nano-sized product, the Fe3 O4 catalyst was oxidized and became the core of the product.关键词
纤维素/Fe3 O4/水热法/碳化Key words
cellulose/Fe3 O4/hydrothermal treatment/carbonization分类
化学化工引用本文复制引用
江浩,杨继涛,胡国新,黄浩..Fe3 O4催化纤维素水热法制备 Fe2 O3/碳纳米复合材料[J].表面技术,2014,(4):115-118,134,5.基金项目
高等学校博士学科点专项科研基金项目(20100073110036)Fund：Supported by the Specialized Research Fund for the Doctoral Program of Higher Education(20100073110036) （20100073110036）