电子器件Issue(6)：1021-1025,5.DOI:10.3969/j.issn.1005-9490.2014.06.002
用于AC-PDP保护层的六硼化镧薄膜的制备与性能研究∗
The Characteristics of the Lanthanum Hexaboride Thin Films Applied in Protective Layer of AC-PDP
摘要
Abstract
The LaB6 thin film was deposited on MgO protective layer of PDP by the screen-printing method. The sur-face appearance and the optical performance of LaB6/MgO films fabricated with different process parameters were tested. Besides, the discharge performance of the LaB6/MgO film with high transmittance was tested in Xe/Ne mixed gases. It is shown that the screen of 400 meshes and the ball-milled LaB6 are benefit to improve the visible light transmittance. Using the conventional MgO protective layers as a reference,the visible light transmittance of LaB6/MgO film reaches at a high level of 90%. The consequence of the discharge test has shown that the discharge performance of the MgO substrate printed with the LaB6 thin film is better than the traditional MgO protective layer. The firing voltage and discharge delay time have been descended by 7% and 9%,respectively.关键词
PDP/丝网印刷/透过率/着火电压/放电延迟Key words
PDP/screen-printing/transmittance/firing voltage/discharge delay time分类
信息技术与安全科学引用本文复制引用
徐晓,王怡,牛童,王小菊..用于AC-PDP保护层的六硼化镧薄膜的制备与性能研究∗[J].电子器件,2014,(6):1021-1025,5.基金项目
中央高校科研基本业务费项目( ZYGX2010J062) （ ZYGX2010J062）
四川省科技创新苗子工程项目 （）