金刚石与磨料磨具工程Issue(3)：57-60,75,5.DOI:10.13394/j.cnki.jgszz.2015.3.0011
K9玻璃磁性研磨抛光表面粗糙度试验研究
Research on surface roughness of K9 glass by magnetic abrasive finishing
丘永亮 1邱腾雄 1阎秋生2
作者信息
- 1. 广东工贸职业技术学院，广州 510510
- 2. 广东工业大学 机电工程学院，广州 510090
- 折叠
摘要
Abstract
To study the existing problems of polishing K9 optical glass,magnetic abrasive finishing was put forward in polishing optical glass•Results showed that surface roughness R a of K9 glass decreased from 90 nm to 40 nm•Based on the feasibility study,the magnetic abrasive finishing experiments were performed by orthogonal experiment with 4 parameters•Then various factors of magnetic abrasive finishing were listed in sequence•The optimum combination was that:pole speed of 2300 r∕min,working clearance of 1•5 mm,magnetic flux density of 0•4 T and feed rate of 200 mm∕min.关键词
磁性研磨/光学玻璃/磁感应强度Key words
magnetic abrasive finishing/optical glass/magnetic flux density分类
矿业与冶金引用本文复制引用
丘永亮,邱腾雄,阎秋生..K9玻璃磁性研磨抛光表面粗糙度试验研究[J].金刚石与磨料磨具工程,2015,(3):57-60,75,5.