激光熔覆铁基涂层工艺参数的研究
Process parameters of laser cladding iron-based coating
摘要
Abstract
Comparative experiments of friction and wear were performed on MM-P2-screen friction and wear tester using laser cladding iron-based coating as the object of study. The morphology of cladding layer under different process parameters were studied by analyzing the changes of wear amount and cladding coating. The results show that the surface hardness are above 62 HRC after cladding coating, far higher than the hardness of substrate. Scanning speed and laser power are the most important factors affecting the morphology and quality of cladding layer. Energy density characterization results show the best abrasion resistance occurs when the energy density is around 60 J/mm2. The scope of the optimal process parameters are: laser power approximately 3.2 kW, the scanning speed around 300 mm/min. The results show that too high laser power and scanning speed also decrease the abrasion resistance of cladding layer.关键词
激光熔覆/熔覆层/工艺参数/耐磨性Key words
laser cladding/cladding layer/process parameters/wear resistance分类
矿业与冶金引用本文复制引用
邓居军,刘政,朱涛..激光熔覆铁基涂层工艺参数的研究[J].有色金属科学与工程,2015,(3):51-55,60,6.基金项目
江西省教育厅重点科技资助项目 （）