（K0．5Na0．5）NbO3-CaZrO3基无铅压电陶瓷的相结构和压电性能研究
Phase Structure and Piezoelectric Properties of (K0.5 Na0.5)NbO3-CaZrO3 Lead-free Piezoelectric Ceramics
潘永军 1王锋会 2刘琨1
作者信息
- 1. 西安金戈磨料磨具有限责任公司 西安 710600
- 2. 西北工业大学工程力学系 西安 710072
- 折叠
摘要
Abstract
Lead-free piezoelectric ceramics (1-x)(K0.5 Na0.5 )NbO3-xCaZrO3 (KNN-CZ)were prepared by traditional ce-ramics process.The phase structure of ceramics was analyzed.Results show that all specimens exhibit a pure perovskite structure and the phase structure at room temperature changes from orthorhombic to tetragonal phase,then to cubic phase with increasing amount of CaZrO3 .The effect of CaZrO3 content on piezoelectric properties was investigated in details. When the content of CaZrO3 is 0.05 mol,d33 and kp reach their maxmum.In addition,good temperature stability of electri-cal properties is obtained in (1-x)KNN-xCZ (x=0.05)ceramics These results indicate that(1-x)KNN-xCZ (x=0. 05)ceramic is a promising lead-free piezoelectric candidate materials.关键词
无铅压电陶瓷/铌酸钾钠/压电性能Key words
Lead-free piezoelectric ceramics/(K0.5 Na0.5 )NbO3/Piezoelectric properties分类
信息技术与安全科学引用本文复制引用
潘永军,王锋会,刘琨..（K0．5Na0．5）NbO3-CaZrO3基无铅压电陶瓷的相结构和压电性能研究[J].陶瓷,2014,(4):23-26,4.