常压干燥制备疏水性 Si O2-玻璃纤维复合气凝胶及表征OA北大核心CSCDCSTPCD
Preparation and Characterization of Hydrophobic SiO2-glass Fibers Aerogels v ia Ambient Pressure Drying
以正硅酸乙酯(TEOS)和甲基三乙氧基硅烷(MTES)为复合硅源,玻璃纤维为增强体,采用溶胶‐凝胶和常压干燥工艺制备出疏水性SiO2‐玻璃纤维复合气凝胶。利用N2吸附脱附、扫描电镜、高分辨透射电镜、红外光谱、接触角、热重‐差热分析及力学测试等手段表征复合气凝胶,并分析预处理玻璃纤维时的盐酸浓度及浸泡时间对复合气凝胶密度的影响。结果表明:当玻璃纤维的预处理条件为2.5mol/L盐酸浸泡0.5h时,制备得到的SiO2‐玻璃纤维复合气凝胶表观密度最低,…查看全部>>
Hydrophobic SiO2‐glass fibers aerogels were prepared by sol‐gel process with tetraethoxysil‐iane (TEOS) and methyltriethoxysilane (MTES) as the silica source ,glass fibers as reinforcement , followed by ambient pressure drying .The physical properties and microstructure of silica aerogels were characterized by nitrogen adsorption/desorption tests ,Fourier transform infrared spectroscopy , thermogravimetric and differential thermal analysis , scanning electro…查看全部>>
余煜玺;吴晓云;伞海生
厦门大学材料学院材料科学与工程系福建省特种先进材料重点实验室,福建厦门361005 厦门大学萨本栋微米纳米技术研究院,福建厦门361005厦门大学材料学院材料科学与工程系福建省特种先进材料重点实验室,福建厦门361005
数理科学
SiO2 气凝胶玻璃纤维常压干燥
silica aerogelglass fiberambient pressure drying
《材料工程》 2015 (8)
共振腔增强等离子体红外光源及其在碳-13呼吸检测法中的应用研究
31-36,6
国家自然科学基金资助项目(51175444,61274120);中央高校(厦门大学)基本科研业务费专项资金资助项目(2011121002);航空科学基金资助项目(2013ZD68009);福建省高等学校新世纪优秀人才支持计划资助项目(2013);福建省自然科学基金资助项目(2014J01206);厦门市科技计划资助项目(3502Z20143009)
评论