摘要
Abstract
This paper describes the effect of plastic deformation on occurrence of abnormal fracture during DWTT using various steels with different microstructures. Each DWTT was carried out at the same test temperature using 20 mm plates with approximately the same tensile strength. This paper describes the deformation during DWTT, which consists of deformation caused by hammer impact, bending compression, and bending tension. The deformation due to the impact of the hammer during DWTT on a 20 mm plate was limited, and the location affected by the hammer impact did not correspond to that where abnormal fracture occurred. Moreover, the equivalent plastic strain from bending deformation was dominant as compared with that of hammer impact regardless of the microstructure. This suggests that abnormal fracture occurred by exceeding the critical equivalent plastic strain due to the bending deformation.关键词
高强度管线钢/DWTT/异常断口/塑性变形/应变当量Key words
high strength pipeline steel/DWTT/abnormal fracture/plastic deformation/strain equivalent分类