某电厂轴承弹簧断裂分析
Fracture Analysis on Bearing Spring of One Power Plant
李海霞 1张小伍 1王梅英 1李兴东1
作者信息
- 1. 哈尔滨汽轮机厂有限责任公司，哈尔滨 150046
- 折叠
摘要
Abstract
The bearing spring of lower part on a turbine of one power plant had fractured.By means of chemical compositions analysis,hardress test,metallographic inspection and fracture surface analysis,the fracture reasons of the bearing spring were researched.The results show that the fracture mechanism of the bearing spring was fatigue fracture.The fracture failure of the spring was due to original defect of spring surface and corrosive medium in the service environment.关键词
轴承弹簧/疲劳断裂/腐蚀Key words
bearing spring/fatigue fracture/corrosion分类
机械制造引用本文复制引用