膜层厚度对Ag/TiO膜透光隔热性能的影响
Effects of Film Layer Thickness on Transmittance and Thermal Insulation of Ag/TiO2 Films
摘要
Abstract
The Ag/TiO2 film was prepared on glass substrate by magnetron sputtering, and the effects of film layer thickness on transmittance and thermal insulation of Ag/TiO2 films were studied. Results showed that the average transmit-tance of infrared light decreased from 42.06% to 7.70% and the temperature difference increased from 1.9℃ to 5.7℃ with the increase of Ag film’s thickness from 6.7 nm to 9.5 nm, while the average transmittance of visible light firstly increased and then decreased. The average transmittance of visible light was up to a maximum of 70.85% at the Ag film’s thickness of 7.7nm. The average transmittance of infrared light increased from 34.12% to 38.28%, while the average transmittance of visible light and the temperature difference firstly increased and then decreased with the increase of TiO2 film’s thickness from 4.1 nm to 16.7 nm. The average transmittance of visible light was up to a maximum of 70.85% at the TiO2 film’s thickness of 10.4 nm, and the temperature difference was up to a maximum of 5.2℃ at the TiO2 film’s thickness of 13.6 nm.关键词
Ag/TiO2膜/透光率/隔热温差/光学性能Key words
Ag/TiO2 film/transmittance/thermal insulation temperature difference/optical property分类
数理科学引用本文复制引用
丁泽良,陈飞龙,黄志翔,杨益辉..膜层厚度对Ag/TiO膜透光隔热性能的影响[J].包装学报,2016,8(2):15-19,5.基金项目
湖南省自然科学基金资助项目（2015JJ5019），湖南省研究生科研创新基金资助项目 （）