PC/ASA合金的研发
Research on PC/ASA Alloy Performance and Preparation Process
黄李胜 1李景 1麦伟宗 1赖世亮1
作者信息
- 1. 广州合成材料研究院有限公司，广东广州510665
- 折叠
摘要
Abstract
Using a twin-screw extruder equipment,PC/ASA alloy was prepared,the effects of different ratio of PC and ASA on performance were investigated. The results showed that:in PC/ASA system,PC and ASA ratio is 70∶30,adding compatibility agent SMA 4% and 0. 8% of antioxidant and lubricant,can achieve optimal perform-ance:Izod notched impact strength of 66. 7kJ/m2 , the tensile strength of 56. 1MPa, the bending strength of 82. 3MPa,heat distortion temperature of 105. 6℃;while PC/ABS was prepared under the same conditions,PC/ASA alloy has better lightfastness than PC/ABS.关键词