理化检验-物理分册2016，Vol.52Issue(5)：315-319,5.DOI:10.11973/lhjy-wl201605007
锌铝合金时效处理后硬度降低的原因分析
Reasons Analysis on Hardness Reduction of Zinc-aluminium Alloy after Aging Treatment
江河1
作者信息
- 1. 深圳市美信检测技术股份有限公司，深圳 518108
- 折叠
摘要
Abstract
Aiming at the issue of hardness reduction of some N type zinc-aluminium alloy after aging treatment,the zinc-aluminium alloy specimens were analyzed by hardness testing,chemical composition analysis, metallographic inspection,SEM analysis,EDS analysis,material heat treatment performance analysis and heat treatment verification testing.The results show that the N type zinc-aluminium alloy was developed on basis of the ZA50 type zinc-aluminium alloy series.The main reasons of hardness reduction after heat treatment were that the temperature of aging treatment was too high and the holding time of aging treatment was too long,causing the overaging phenomenon.At the end,some improving methods were suggested to meet the hardness requirement of the zinc-aluminium alloy.关键词
锌铝合金/硬度降低/固溶处理/时效处理Key words
zinc-aluminium alloy/hardness reduction/solution treatment/aging treatment分类
矿业与冶金引用本文复制引用
江河..锌铝合金时效处理后硬度降低的原因分析[J].理化检验-物理分册,2016,52(5):315-319,5.