氟硅丙烯酸酯共聚乳液整理亚麻织物的研究
Research on finishing flax fabric with fluorosilicone acrylate copolymer emulsion
隋智慧 1杨康乐 2陈杰 1庞薇薇 1赵欣 1冯元浩1
作者信息
- 1. 齐齐哈尔大学轻工与纺织学院，黑龙江齐齐哈尔 161006
- 2. 齐齐哈尔大学亚麻加工技术教育部工程研究中心，黑龙江齐齐哈尔 161006
- 折叠
摘要
Abstract
The flax fabrics were finished using self-made fluorosilicone acrylate copolymer emulsion. The effects of curing temperature and time on fabrics properties were researched. The finished flax fabrics were tested by ATR-FTIR, XPS, SEM, and water contact angle respectively. The results showed that the optimum effect of flax fabrics finished with fluorosilicone acrylate copolymer emulsion was obtained at 160℃for 3 min. The surface of finished fabrics was smooth and flat. Furthermore, the fabrics possessed better hydrophobicity than that treated with pure acrylate emulsion.关键词
含氟硅丙烯酸酯/乳液聚合/亚麻织物/织物整理/疏水性Key words
fluorosilicone acrylate/emulsion polymerization/flax fabrics/fabrics finishing/hydrophobici分类
轻工纺织引用本文复制引用