Al含量对变形铅室温再结晶行为的影响
Effect of Al content on re-crystallization behavior of lead at room temperature
摘要
Abstract
The effect of aluminum content on the re-crystallization behavior of lead was studied by applying uni-versal testing machine and cold cathode field emission scanning microscope. The results show that the addition of Al can affect the lead's re-crystallization behavior and improve its tensile strength. When the content of Al is 0.05%, the re-crystallization behavior is inhibited obviously and the tensile strength increases from 13.2 MPa to 17.9 MPa. However, when Al content is increased to 0.10 %, the inhibition effect weakens, and the tensile strength declines from 17.9 MPa to 15.5 MPa.关键词
铅铝合金/抗拉强度/再结晶/金属间化合物Key words
lead alloy/tensile strength/re-crystallization/inter-metallic compound分类