低密度高强度炭材料的制备研究
Research and Preparation of Low-density High-strength Carbon Material
夏金童 1王双 1赵海霞 1赵庆才 2赵敬利 2李允柱 2刘奉来2
作者信息
- 1. 湖南大学材料科学与工程学院，湖南长沙 410082
- 2. 肥城昌盛特种石墨有限公司，山东肥城 271600
- 折叠
摘要
Abstract
High strength carbon materials were made with activated petroleum coke powder as the raw material ,coal pitch as the binder under different molding pressures and holding time . The mechanical properties of the samples were tested ,and SEM ,TG‐DTA ,XRD were analyzed .The interaction mecha‐nism of the raw materials and the binder was clarified .The results have shown that ,the properties of the roasted samples increase with the pressure holding time and the molding pressure .In the holding time of 20 min ,the molding pressure is 200 MPa ,the bulk density of the roasted sample reaches 1 .54 g/cm3 ,the compressive strength is 119 MPa and the flexural strength is 61 MPa .They are all better than the samples made without activated petroleum coke powder as the raw material .关键词
活化/石油焦粉/高强度/成型压力/保压时间Key words
activation/petroleum coke powder/high-strength/molding pressure/holding-time分类
信息技术与安全科学引用本文复制引用
夏金童,王双,赵海霞,赵庆才,赵敬利,李允柱,刘奉来..低密度高强度炭材料的制备研究[J].湖南大学学报（自然科学版）,2016,43(6):58-63,6.