电工技术学报2016，Vol.31Issue(18)：191-198,8.
氧化铝/环氧树脂复合材料空间电荷特性与高温高湿环境下交流电场老化
Space Charge and AC Field Aging in High Hygrothermal Environment of Alumina/Epoxy Resin Composites
摘要
Abstract
Micro- and nano-alumina/epoxy resin composites were prepared in laboratory. The effects of different particle diameters and contents on space charge of epoxy resin composites were analyzed in this paper. The space charge distribution of experimental samples was measured before and after AC aging in high hygrothermal environment, to reveal the effects of alumina on electrical characteristics of composites. It is found that more space charges appeared in micro-composites and nano-composites with the increasing of alumina particles content. The sedimentation phenomenon of micro-alumina particles is more obvious in the samples of micro-alumina/epoxy resin composites than that in the samples of room temperature curable epoxy resin. The samples of micro-alumina/epoxy resin composites show different contents of micro-alumina between the up and down layers. Under the environment of 80℃ and 90% RH, the space charges were detected again after AC aging at 20kV/mm. It is shown that the withstanding aging ability of nano-composite is stronger than those of neat epoxy and micro-composite.关键词
氧化铝/环氧树脂/复合材料/老化/空间电荷Key words
Alumina/epoxy resin/composite/aging/space charge分类
信息技术与安全科学引用本文复制引用
龚瑾,李喆,刘新月..氧化铝/环氧树脂复合材料空间电荷特性与高温高湿环境下交流电场老化[J].电工技术学报,2016,31(18):191-198,8.基金项目
国家自然科学基金资助项目（51007057）。 （）