氮化硅陶瓷的无压烧结工艺优化及性能研究OA北大核心CSCDCSTPCD
Process Optimization and Properties of Silicon Nitride Ceramics Prepared by Pressureless Sintering
以α-Si3 N4为原料，Y2 O3和MgO为复合烧结助剂，通过无压烧结制备出氮化硅陶瓷。为了优化实验配方和工艺参数，采用正交实验研究了成型压力、保压时间、保温时间、烧结温度、烧结助剂含量以及配比对氮化硅陶瓷气孔率和抗弯强度的影响规律。结果表明，影响氮化硅陶瓷气孔率的主要因素是烧结助剂含量和配比，而影响其抗弯强度的主要因素是烧结助剂配比和烧结温度。经分析得出，最佳工艺参数为成型压力16 MPa，保压时间120 s，保温时间2 h，烧结温度1750…查看全部>>
Silicon nitride ceramics were prepared by pressureless sintering , using α-Si3 N4 as raw material, Y2 O3 and MgO as sintering additives .In order to optimize the experiment formulation and process parameters , the effects of forming pressure , pressure-holding time , holding time , sintering temperature , the content and the ratio of sintering additives on the apparent porosity and bending strength of the silicon nitride ceramics were investigated by using t…查看全部>>
王欢;玄伟东;杨治刚;马晨凯;赵登科;任忠鸣;王保军;王江
上海大学省部共建高品质特殊钢冶金与制备国家重点实验室，上海 200072 上海市钢铁冶金新技术应用重点实验室，上海 200072上海大学省部共建高品质特殊钢冶金与制备国家重点实验室，上海 200072 上海市钢铁冶金新技术应用重点实验室，上海 200072上海大学省部共建高品质特殊钢冶金与制备国家重点实验室，上海 200072 上海市钢铁冶金新技术应用重点实验室，上海 200072上海大学省部共建高品质特殊钢冶金与制备国家重点实验室，上海 200072 上海市钢铁冶金新技术应用重点实验室，上海 200072
矿业与冶金
氮化硅正交实验气孔率抗弯强度
silicon nitrideorthogonal experimentporositybending strength