碳纤维缠绕成型用高性能环氧树脂基体的研究
Study on High Performance Epoxy Resin for Filament Winding Technology
杨刚1
作者信息
- 1. 蓝星纤维(北京)有限公司,北京100029
- 折叠
摘要
Abstract
In the present study,two kinds of epoxy resins,MHR-070 and TDE-85,were mixed together in a proportion,and then liquid curing agent with low viscosity and a diluent agent were added,obtained an epoxy resin for filament winding. Experimental results indicated that the resin system had viscosity of 609 mPa·s at 25℃ and service life exceed 8h. The cured resin system showed good properties with tensile strength of 93. 5MPa,tensile modulus of 2. 7GPa and Tg of 197. 5℃,which can be used for filament winding. The T700 carbon fiber reinforced composite also had good mechanical properties.关键词
环氧树脂/耐高温/缠绕成型Key words
epoxy resin/high temperature resistance/filament winding引用本文复制引用
杨刚..碳纤维缠绕成型用高性能环氧树脂基体的研究[J].合成材料老化与应用,2016,45(5):33-35,82,4.