Research on Preparation and Corrosion Resistance of Superhydrophobic Surfaces on Carbon Steels
通过喷砂与电刷镀相结合的方法在碳钢表面制备出未经修饰的微纳双尺度复合结构的超疏水表面。利用扫描电子显微镜(SEM)、接触角测量仪、电化学工作站对表面形貌、动静态接触角以及耐腐蚀性进行观测。结果表明：采用该结合方法制备的疏水表面在晶粒簇直径为25~40μm,且分布均匀时,具有优异的超疏水性能；当制备电压在14V时,接触角达到152°,同时在自然时效状态下,试样能够长时间保持表面的疏水特性；结合方法制备的疏水表面与基底抛光表面相比,耐腐蚀性能提高。
Superhydrophobic surfaces on carbon steels were fabricated combining sandblasting and electro-brush plating technology without modification.The surface appearance,dynamic and static contact angles and anti-corrosions were characterized by means of scanning electron microscopy (SEM),contact angle measuring instrument and electrochemical workstation.The results show that the superhydrophobic surfaces prepared by the combination method are obtained when the dia…查看全部>>
李晶;李红;于化东;杜锋
长春理工大学，长春，130022长春理工大学，长春，130022长春理工大学，长春，130022装甲兵技术学院，长春，130117
矿业与冶金
综合技术超疏水碳钢耐腐蚀
combining technologysuperhydrophobiccarbon steelcorrosion resistance
《中国机械工程》 2016 (23)
微机械制造-脉冲沉积复合构建仿生疏水耦合结构及演化机制研究
3241-3245,3246,6
国家自然科学基金资助项目(51505039)吉林省科技发展计划资助项目(20150204018GX)中国博士后科学基金资助项目(2014M551145)
评论