材料工程2017，Vol.45Issue(2)：32-38,7.DOI:10.11868/j.issn.1001-4381.2015.000579
多层金属复合板的热轧制备方法
Hot-rolled Process of Multilayered Composite Metal Plate
余伟 1王班 1贺婕 1徐士新 1雷力齐1
作者信息
- 1. 北京科技大学冶金工程研究院 ,北京100083
- 折叠
摘要
Abstract
For multi-layer plate ,it is a difficult problem to increase product yield rate and improve bonding interface quality .A high yield hot-rolled method of multilayered plate was proposed .The raw strips and plate were fixed by argon arc welding .The combined billet was put into a metal box and vacuum pumped ,and then heated and rolled by multi passes at the temperature of 1000-1200℃ .The 67 layered plate with the thickness of 2 .5mm was successfully produced .The interfacial microstruc-tures and diffusion behavior were investigated and analyzed by optical microscopy and scan electronic microscopy .The tensile and shear strength were tested ,and the shear fractures were analyzed .The results show that the multilayered plate yield rate is more than 90% by two steps billet combination method and rolling process optimization .The good bonding interface quality is obtained ,the shear strength of multilayered plate reaches 241MPa .Nickel interlayer between 9Cr18 and 1Cr17 can not only prevent the diffusion of carbon ,but also improve the microstructure characteristics .关键词
多层金属复合板/热轧工艺/组织/力学性能/扩散Key words
multilayered plate/hot-rolled process/microstructure/mechanical property/diffusion分类
矿业与冶金引用本文复制引用
余伟,王班,贺婕,徐士新,雷力齐..多层金属复合板的热轧制备方法[J].材料工程,2017,45(2):32-38,7.