陶瓷Issue(1)：30-34,5.
添加铁粉制备低密度中强度陶粒支撑剂及性能研究
Preparation and Mechanisms of Light-weight Middle-strength Ceramisite Proppant by Iron Powder Additive
刘挺 1王菊侠 1曹义平 1庞锐 1赵爽 1王超1
作者信息
- 1. 陕西省石油化工研究设计院 西安 710048
- 折叠
摘要
Abstract
Light-weight middle-strength ceramisite proppant is beneficial to the improvement of productivity of low-permeability oil and gas reservoir,and is able to reduce the cost of oil and gas production significantly.The light-weight middle-strength ceramisite proppant was prepared from bauxite(63 wt％ Al2O3) by adding manganese mineral,part of that was replace by iron powder.The results show that strength of ceramisite proppant was improved by rod-like mullite with the diameter of 0.3 ～ 1.0μm,which playa remarkable role in the increment of fracture toughness,when iron powder content is 3 wt％,and manganese mineral content is 2 wt％,and dolomite content is 1 wt％ and sintering at 1 350 ℃ for 1 h.The breakage ratio is 5.29％ and bulk density was 1.63 g/cm3 under 52 MPa closure pressure.In addition,as the iron powder increase,he liquid phase increase in the matrix,many intergranular closed pores were formed as a result of the grain growth which was too speedy to eliminate pores.It is easy to form the crack source and reduce the density and strength of ceramisite proppant.关键词
陶粒支撑剂/低密度/中强度/铁粉/锰矿Key words
Ceramisite proppant/Light-weight/Middle-strength/Iron powder/Manganese mineral分类
通用工业技术引用本文复制引用
刘挺,王菊侠,曹义平,庞锐,赵爽,王超..添加铁粉制备低密度中强度陶粒支撑剂及性能研究[J].陶瓷,2017,(1):30-34,5.