Chrysotile Fiber Reinforced Lightweight Porous Diatoms Brick
摘要
Abstract
Lightweight porous diatoms brick was prepared through compression molding and calcination using diatomite,chrysotile and kaolin as raw materials.The systematic investigations on the bulk density,water absorption,porosity,rupture modulus and moisture absorption-desorption of the diatomite brick were carried out.The structure and morphology of the diatomite brick were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM),respectively.The results show that water absorption and porosity of the diatomite brick decrease with the increase of chrysotile content and calcination temperature.On contrary,the rupture modulus of the diatomite brick was increased significantly.The rupture modulus,bulk density and apparent porosity of the diatoms brick are 10 MPa,1.18 g/cm3 and 47.97%,respectively,when the chrysotile content and calcination temperature are 10wt% and 900 ℃.These indicate that the diatomite brick has the prominent advantage of high strength,light weight,porous and well moisture absorption-desorption properties.关键词
纤蛇纹石纤维/硅藻土/轻质多孔砖Key words
chrysotile fiber/diatomaceous earth/lightweight porous brick分类
化学化工引用本文复制引用
刘欢,刘琨,唐学昆,卢佳..纤蛇纹石纤维增强轻质多孔硅藻砖[J].硅酸盐通报,2017,36(4):1169-1174,1186,7.基金项目
湖北省科技厅项目(2012BAA1001) （2012BAA1001）