熔盐提拉法生长大尺寸KGW晶体及其拉曼特性研究OA北大核心CSCDCSTPCD
Growth and Raman Characteristics of Large Size KGW Crystal by TSSG Method
β-KGd(WO4)2(简称KGW)晶体是一种兼具激光基质和拉曼性能的优秀材料,受到了广泛的关注和研究.采用熔盐提拉法生长了尺寸>60 mm、质量>800 g的KGW晶体,光学均匀性为1.34×10-5.在生长的晶体中,观察到了包裹体聚集层、空洞和开裂等较大尺寸缺陷,并探讨了原因.初步的激光实验实现了1151.3 nm拉曼激光输出,功率80 mW,拉曼频移为898.2 cm-1.
β-KGd(WO4)2 crystal attracts a lot of attention owing to its excellent properties for acting as both laser host and Raman gain medium.High optical-quality KGW crystals were grown by the TSSG (top-seeded solution-growth) method, with the size larger than 60 mm and the weight more than 800 g, and the optical homogeneity was measured to be 1.34×10-5.During the processes of crystal growth, several defects such as inclusions, holes and cracks were observed, and t…查看全部>>
朱昭捷;孙益坚;李坚富;游振宇;王燕;涂朝阳
中国科学院福建物质结构研究所,中国科学院光电材料化学与物理重点实验室,福州 350002中国科学院福建物质结构研究所,中国科学院光电材料化学与物理重点实验室,福州 350002中国科学院福建物质结构研究所,中国科学院光电材料化学与物理重点实验室,福州 350002中国科学院福建物质结构研究所,中国科学院光电材料化学与物理重点实验室,福州 350002中国科学院福建物质结构研究所,中国科学院光电材料化学与物理重点实验室,福州 350002中国科学院福建物质结构研究所,中国科学院光电材料化学与物理重点实验室,福州 350002
数理科学
KGW晶体熔盐提拉法晶体生长拉曼激光
KGW crystalTSSG methodcrystal growthRaman laser
《人工晶体学报》 2017 (4)
3μm以上中红外可调谐激光用的Dy3+:LnF3晶体的制备与性能系统研究
573-577,5
国家自然科学基金(61675204,51472240)福建省国际合作项目(2015I0007)福建省自然科学基金(2016J01274,2015J05134)
评论