印染助剂2017，Vol.34Issue(6)：10-14,5.
纳米复合抗紫外有机硅整理剂的制备及应用研究
Preparation and application of nano composite anti-UV silicone finishing agent
摘要
Abstract
A novel polyether/UV/alkoxy co- modified phenyl silicone oil (VPE- BUVSi) was synthesized in the solvent of isopropanol. The compound emulsion UVAS was prepared by VPE- BUVSi emulsion and ASO emulsion (AS- 1). The cotton fabric was treated by nano- silica sol SW- 30 and UVAS in turn to obtain a na-no- composite anti- UV silicone finishing agent. The intermediates and related products were studied by infra-red spectrum (IR), ultraviolet spectrum (UV), scanning electron microscope (SEM) and nano particle size instru-ment. The results showed that when the mass ratio of VPE- BUVSi emulsion and AS- 1 were 6:4, the effect of anti- UV capability, anti- aging properties, softness, whiteness and elasticity were the best. Compared with the blank fabric, UV transmittance of treated fabric was significantly decreased. Bending rigidity of treated fab-ric decreased from 1068 mN to 961 mN. Wrinkle recovery angle increased from 144.14° to 210.33° . White-ness were unaffected. The treated fabric had good anti- UV properties. The nano- composite anti- UV silicone finishing agent could give the fabric a certain anti- UV and anti- wrinkle performance under the premise of keeping the fabric soft feel.关键词
纳米复合/改性苯基硅油/棉织物/复配/抗紫外Key words
nano- composite/modified phenyl silicone oil/cotton fabric/compounding/anti- UV分类
化学化工引用本文复制引用
李海波,安秋凤,李晓璐,李聪..纳米复合抗紫外有机硅整理剂的制备及应用研究[J].印染助剂,2017,34(6):10-14,5.基金项目
陕西省科技厅科技统筹项目(2015KTCL01-14) （2015KTCL01-14）
陕西省教育厅服务地方专项计划项目(16JF004) （16JF004）