硅酸盐通报2017，Vol.36Issue(6)：1830-1834,5.
碱激发矿渣基地质聚合物微观结构与性能研究
Microstructure and Properties of Alkali-activated Blast Furnace Slag Based Geopolymer
摘要
Abstract
Blast furnace slag (BFS) based geopolymer were prepared by using blast furnace slag as raw material, and effects of different SiO2/Al2O3 ratio on the properties and microstructure of BFS based geopolymers were studied.BFS based geopolymer were prepared with SiO2/Al2O3 ratio of 4.5, 4.8, 5.1, 5.4, and detected by XRF、XRD、SEM、TEM、FTIR, it reveals that BFS based geopolymer exhibit high compressive strength of 97.86 MPa、97.54 MPa, and 114.91 MPa at 3 d, 7 d, and 28 d with SiO2/Al2O3 ratio of 5.1, the main products are the mixture of N,C-A-S-H and C-S-H.关键词
矿渣/地质聚合物/微观结构Key words
slag/geopolymer/microstructure分类
建筑与水利引用本文复制引用
刘泽,周瑜,孔凡龙,孙志明,屈美秀..碱激发矿渣基地质聚合物微观结构与性能研究[J].硅酸盐通报,2017,36(6):1830-1834,5.基金项目