高铝玻璃减薄优化工艺研究
Study on the optimization of high alumina glass thinning
摘要
Abstract
On the basis of chemical etching technology,the optimization of the thinning of high alumina glass was studied.Under the protection of the photoresist and sealant,the following results were obtained under pH =2,temperature 55 ℃ and the etching time of 45min.The as-obtained samples were characterized by Field-Emission Scanning Electron Microscope (FE-SEM),Energy Dispersive X-ray Detector (EDX).And a series of conditional experiments were done.Under the optimal conditions,the results showed that the reduction rate of the glass substrate was obviously increased,the surface roughness was effectively reduced,and the precipitation of the white precipitates was decreased.It provides a feasibility plan for flat glass,display panels and other industries manufacturing.关键词
高铝玻璃/玻璃减薄/减薄液/品质分析Key words
high alumina glass/glass thinning/thinning fluid/quality analysis分类
化学化工引用本文复制引用
李运涛,牛俊丽,许淑嫱,刘存海..高铝玻璃减薄优化工艺研究[J].陕西科技大学学报,2017,35(3):86-89,100,5.基金项目
陕西省科技厅工业科技攻关计划项目(2016GY-142) （2016GY-142）