锌-钆抗菌白炭黑粉体的改性及抗菌性能研究
Modification and Antibacterial Properties of Zinc-Gadolinium Antibacterial White Carbon Black
摘要
Abstract
Zinc-Gadolinium antimicrobial white carbon black was prepared by sol-gel method.The materials were modified by adding surfactants.And the changes of particle size, specific surface area and antibacterial property were investigated before and after the modification.The samples were characterized by particle size analysis, BET, SEM and EDS.The results show that the particle size of the modified material decreases, and the particle size distribution is relatively concentrated.The specific surface area increase to 275.20209 m2/g.Antibacterial test results show that the antibacterial property of the modified material is enhanced.And antibacterial rate of Zinc-Gadolinium antimicrobial white carbon black can reach above 90.29％.关键词
无机抗菌材料/白炭黑/钆/锌/改性Key words
inorganic antibacterial material/white carbon black/gadolinium/zinc/modification分类
建筑与水利引用本文复制引用
张彬,胡艳玲,李欢,唐晓宁,郭一婧,杨和山..锌-钆抗菌白炭黑粉体的改性及抗菌性能研究[J].硅酸盐通报,2017,36(8):2714-2719,6.基金项目
国家自然科学基金(21677010) （21677010）
昆明理工大学分析测试基金(2016T20110234) （2016T20110234）