中国组织工程研究2017，Vol.21Issue(22)：3483-3487,5.DOI:10.3969/j.issn.2095-4344.2017.22.007
应用微纤维胶原支架构建组织工程软骨
Tissue-engineered cartilage construction using microfibrillar collagen
摘要
Abstract
BACKGROUND:To seek for ideal scaffold materials is still an important task for cartilage tissue engineering.OBJECTIVE:To investigate the application of the AviteneTM microfibrillar collagen hemostat sponge in cartilage tissue engineering.METHODS:Rabbit auricular cartilage was harvested via surgical operation,and primary chondrocytes were isolated and amplified.Microfibrillar collagen hemostat sponge was cut into small bricks.The passage 2 chondrocytes were suspended and seeded onto the spongy bricks.After 1 week of in vitro culture,the constructs were then implanted into nude mice.After 8 weeks,the specimens were collected and evaluated using gross,histological and immunohistochamical observation.RESULTS AND CONCLUSION:During the cell seeding,the scaffold maintained its dimensions.No shrinkage was observed when the cell suspension was added.There was no considerable change in dimensions during the 1-week in vitro culture and at 8 weeks after implantation in nude mice.At 8 weeks post-implantation,mature cartilage blocks were harvested,which were white,translucent,and flexible.Histologically,the constructs appeared to have typical mature cartilaginous tissues,with robust extracellular matrix secretion,in which the microfibrillar collagen was incompletely degraded.We conclude that the microfibrillar collagen is a favorable scaffold material for cartilage tissue engineering.关键词
生物材料/软骨生物材料/微纤维胶原/软骨细胞/软骨/组织工程/国家自然科学基金分类
医药卫生引用本文复制引用
周丽斌,徐冰心,丁瑞英,韩浩伦,王刚,李保卫,王鸿南,吴玮..应用微纤维胶原支架构建组织工程软骨[J].中国组织工程研究,2017,21(22):3483-3487,5.基金项目
国家自然科学基金青年科学基金项目(81401609)the National Natural Science Foundation of China,No.81401609 （81401609）