添加碳化硼对低碳铝碳耐火材料显微结构和性能的影响OA北大核心CSCDCSTPCD
Effect of B4C Additive on Microstructure and Mechanical Properties of Low Carbon Al2O3-C Refractories
以板状刚玉和活性氧化铝微粉为主要原料、纳米炭黑为碳源、碳化硼(质量分数0、0.5%、1%)和单质硅粉为添加剂,制备了低碳铝碳耐火材料.利用X射线衍射仪、场发射扫描电子显微镜分别检测和观察了材料的物相组成和显微结构.采用三点弯曲法研究了材料的常温和高温力学性能,采用水淬冷法研究了材料的热震稳定性.结果表明:与空白试样相比,在1000℃处理的含碳化硼的试样中发现碳纳米管(MWCNTs);温度高于1200℃,在材料表面出现了明显的含氧化硼反应层,形成了…查看全部>>
Al2O3-C refractories were prepared with corundum, alumina powder, carbon black as main raw materials and boron carbide and silicon as additives. The phase composition and microstructures of the prepared materials were characterized by X-ray diffraction and scanning electron microscopy, respectively. Also, the room-temperature and high-temperature mechanical properties were analyzed via three-point bending tests. The thermal shock resistance of Al2O3-C refrac…查看全部>>
刘耕夫;李亚伟;廖宁;桑绍柏
武汉科技大学,省部共建耐火材料与冶金国家重点实验室,武汉 430081武汉科技大学,省部共建耐火材料与冶金国家重点实验室,武汉 430081武汉科技大学,省部共建耐火材料与冶金国家重点实验室,武汉 430081武汉科技大学,省部共建耐火材料与冶金国家重点实验室,武汉 430081
化学工程
碳化硼铝碳耐火材料显微结构力学性能热震稳定性
boron carbidealumina-carbon refractoriesmicrostructuremechanical propertiesthermal shock resistance