首页|期刊导航|中国铸造|Numerical simulation of central shrinkage crack formation in a 234-t steel ingot

Numerical simulation of central shrinkage crack formation in a 234-t steel ingot

Jing-an Yang Yue-qiao Wang Hou-fa Shen Bai-cheng Liu

中国铸造2017，Vol.14Issue(5)：365-372,8.

Numerical simulation of central shrinkage crack formation in a 234-t steel ingot

Jing-an Yang ¹Yue-qiao Wang ²Hou-fa Shen ¹Bai-cheng Liu¹

作者信息

1. School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China
2. Casting and Forging Workshop, China National Erzhong Group Co. Ltd., Deyang 618000, China
折叠

摘要

关键词

shrinkage crack/finite-element/crack potential/thermo-mechanical simulation/steel ingot

Key words

shrinkage crack/finite-element/crack potential/thermo-mechanical simulation/steel ingot

分类

信息技术与安全科学

引用本文复制引用

Jing-an Yang,Yue-qiao Wang,Hou-fa Shen,Bai-cheng Liu..Numerical simulation of central shrinkage crack formation in a 234-t steel ingot[J].中国铸造,2017,14(5):365-372,8.

基金项目

This work was financially supported by the NSFC-Liaoning Joint Fund (U1508215) and the project to strengthen industrial development at the grass-roots level of MIIT China (TC160A310/21). （U1508215）

中国铸造

OACSTPCD

ISSN：1672-6421

访问量0

下载量0

段落导航